B65A1300电工钢标准材质区别零件成型稳定

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Specific total loss (iron loss) is the total power consumed per unit mass of material when the magnetic polarization waveform remains sinusoidal, with a specific peak and frequency. The specific total loss is represented by the symbol P (Jm/f), in W/kg. Example: P1.5/50 represents the specific total loss at a maximum magnetic polarization intensity of 1.5T and a frequency of 50Hz. 3.2 Magnetic Polarization Q/BQB 480-20212 Magnetic polarization intensity refers to the peak magnetic polarization intensity of a specific magnetic field intensity when a sample is subjected to alternating magnetization. Its symbol is J (H), and the unit is T (Tesla). Example: J5000 represents the peak magnetic polarization intensity corresponding to a magnetic field intensity peak of 5000A/m. The material grades in this document are classified based on the nominal maximum specific total loss P1.5/50 (W/kg) at a magnetic polarization strength of 1.5T and a frequency of 50Hz, as well as the nominal thickness of the material. They are further divided into three categories based on product characteristics: ordinary type, stress relief annealing type, and high-efficiency type. Example 1: B35A210 represents a common non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 2.10W/kg； Example 2: B35AR300 represents a stress relieved annealed non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 3.00W/kg； Example 3: B35AH230 represents an efficient non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. Example 4: 35WW210 represents a normal type WW non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.10W/kg. Example 5: 35WH230 represents an efficient WH non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. The classification and code of insulation coatings shall comply with the provisions of Table 2. Table 2 Classification and Code of Insulation Coatings Type Code Characteristics of Insulation Coatings Semi organic Thin Coating A Improves Punching Performance and Has Good Weldability Semi organic Thick Coating H has Good Punching Performance and High Interlayer Resistance Semi organic Chromium Free Thin Coating K does not contain chromium and has good weldability Semi organic Chromium Free Thick Coating M does not contain chromium and has good insulation performance Semi organic Chromium Free Extreme Thick Coating J does not contain chromium and has excellent insulation performance Semi organic Chromium Free Ultra Thick Coating L does not contain chromium and has extremely high insulation performance Self adhesive Coating

电工钢硅钢片电工钢板的磁感应强度高，铁芯的激磁电流（也称空载电流）降低，铜损和铁损都下降，可节省电能。当电机和变压器功率不变时，磁感应强度高，设计Bm可提高，铁芯截面积可缩小，这使铁芯体积减小和重量减轻，并节省电工钢板、吉林长春导线、吉林长春绝缘材料和结构材料用量，可降低电机和变压器的总损耗和制造成本，并且有利于大变压器和大电机的制造、吉林长春安装和运输。硅钢性能的要求主要是：1、吉林长春铁损低，这是硅钢片质量的重要指标。各国都根据铁损值划分牌号，铁损愈低，牌号愈高。2、吉林长春较强磁场下磁感应强度（磁感）高，这使电机和变压器的铁芯体积与重量减小，节约硅钢片、吉林长春铜线和绝缘材料等。3、吉林长春表面光滑、吉林长春平整和厚度均匀，可以提高铁芯的填充系数。4、吉林长春冲片性好，对制造微型、吉林长春小型电动机更为重要。5、吉林长春表面绝缘膜的附着性和焊接性良好，能防蚀和改善冲片性

电工钢硅钢片：密度用于计算磁性能和叠装系数的约定密度为 7.65×103 kg/m3。7.4.2 叠装系数产品的小叠装系数应符合表 3、吉林长春同城表 4、吉林长春同城表 5、吉林长春同城表 6、吉林长春同城表 7、吉林长春同城表 8 和表 9 的规定。7.4.3 弯曲次数产品平行于轧制方向的小弯曲次数应不小于 1 次。供方如能保证，可不进行该试验。7.4.4 由内应力引起的剪切边的偏差产品应尽可能量避免出现内应力。根据需方要求，并在合同中注明，可对宽度不小于 500mm 的材料（纵切分条后的材料）检测由内应力引起的剪切边偏差，其缝隙测量值应不超过 1mm。供方如能保证，可不进行该试验。8 检验和试验8.1 一般要求8.1.1 按本文件签订订货协议时，用户可按GB/T 17505规定进行规定检验和试验或非规定检验和试验。然而，对于非规定检验和试验，制造方应提供所需产品的比总损耗值和磁极化强度值。8.1.2 当按规定检验和试验订货时，用户应明确 GB/T 18253 中的检验文件的类型。